Alumínium-oxiddal erősített szintaktikus fémhabok mikroszerkezetének vizsgálata
Microstructure properties of aluminium reinforced syntactic metal foams
Keywords:
syntactic foams, aluminium oxide, ceramic spherical shell, microstructure properties, infiltration, /, szintaktikus fémhabok, alumínium-oxid, kerámia gömbhéj, mikroszerkezet vizsgálata, infiltrációAbstract
In this research, we have successfully prepared metal matrix reinforced syntactic metal foams. Al99.7 aluminium was used as the matrix material, while Al99.7 aluminium was used as the filler material ceramic hollow sphere (CHS). The reinforcing material was used one size (0.5 mm) aluminium oxide (Al2O3), particles were used as matrix material compared to 5%; 10% and 15% by matrix volume. The microstructure properties were studied.
Kivonat
Kutatásunk során sikeresen gyártottunk mátrixanyagában erősített szintaktikus fémhabokat. Mátrixanyagként Al99,7-es alumíniumot, míg töltőanyagként Al99,7-es kerámia gömbhéjat (CHS) használtunk. Erősítőanyagként 0,5 mm átmérőjű méretű alumínium-oxid (Al2O3) részeket alkalmaztunk a mátrixanyaghoz képest 5%; 10% és 15 térfogatszázalékos térkitöltésben. Kutatásunk során gyártott szintaktikus fémhabok mikroszerkezetét tanulmányoztuk.
References
K. Sun és mtsai., „Preparation and quasi-static compression properties of hybrid aluminum matrix syntactic foam reinforced with glass cenospheres and silicon carbide nanowires”, Mater Charact, köt. 195, o. 112496, jan. 2023, doi: 10.1016/J.MATCHAR.2022.112496.
J. Kumar, S. Negi, és V. Mishra, „3D printed PETG/cenosphere syntactic foam composites for lightweight structural applications”, Mater Lett, köt. 355, o. 135493, jan. 2024, doi: 10.1016/J.MATLET.2023.135493.
L. Zhang és J. Ma, „Effect of carbon nanofiber reinforcement on mechanical properties of syntactic foam”, Materials Science and Engineering: A, köt. 574, o. 191–196, júl. 2013, doi: 10.1016/J.MSEA.2013.03.028.
N. A. B. N. Zamani, A. K. M. Asif Iqbal, és D. M. Nuruzzaman, „Fabrication and characterization of Al2O3 nanoparticle reinforced aluminium matrix composite via powder metallurgy”, Mater Today Proc, köt. 29, o. 190–195, jan. 2020, doi: 10.1016/J.MATPR.2020.05.541.
J. A. Santa Maria, B. F. Schultz, J. B. Ferguson, és P. K. Rohatgi, „Al–Al2O3 syntactic foams – Part I: Effect of matrix strength and hollow sphere size on the quasi-static properties of Al-A206/Al2O3 syntactic foams”, Materials Science and Engineering: A, köt. 582, o. 415–422, okt. 2013, doi: 10.1016/J.MSEA.2013.05.081.
Al99,7 anyagösszetétel táblázat: „https://www.steelnumber.com/en/steel_alloy_composition_eu.php?name_id=1014”. (Utolsó letöltés dátuma: 2024. 02. 21.)