Effect of different surface roughness and the passivation on corrosion and tribological properties of BÖHLER W350 ISOBLOC hot forming tool steel
Keywords:
hot-forming tool steel, duplex surface treatment, surface roughness, corrosion, /, melegalakító szerszámacél, duplex felületkezelés, felületi érdesség, korrózióAbstract
Industrial professionals and academic researchers alike recognize the importance of growing industrial needs and requirements, so they pay special attention to improving the lifetime and performance of materials used in industry. Corrosion protection is of great importance, as neglecting which can cause serious damage to any business. In our research, we subjected the surface of BÖHLER W350 ISOBLOC hot forming tool steel to mechanical and chemical treatments in order to modify the corrosion and tribological properties.
Kivonat
Az ipari szakemberek és az akadémiai kutatók egyaránt felismerik a növekvő ipari igények és követelmények fontosságát, így különleges figyelmet szentelnek az iparban alkalmazott anyagok élettartamának és teljesítményének javítására. Kiemelkedő jelentőségű az iparban a korrózióvédelem, amelynek elhanyagolása súlyos károkat okozhat minden vállalkozásnak. Kutatásunkban BÖHLER W350 ISOBLOC melegalakító szerszámacél felületét vetettük alá mechanikai és kémiai kezeléseknek a korróziós és tribológiai tulajdonságok módosítása érdekében.
References
C. M. Cotell, Jr. et al., ASM handbook. Vol. 5: Surface engineering, ASM International, Materials Park, OH, 1994
Varbai B., Bolyhos P., Kemény D. M., Májlinger K.: Microstructure, Corrosion Properties of Austenitic, Duplex Stainless Steel Dissimilar Joints, Periodica Polytechnica Mechanical Engineering, 2022, 66(4), pp. 344–349
Kemény D. M., Sándor B., Varbai B., Katula L. T.: The Effects of Arc Voltage and Shielding Gas Type on the Microstructure of Wire Arc Additively Manufactured 2209 Duplex Stainless Steel, ADVANCES IN MATERIALS SCIENCE 23, 2023, 4 pp. 62-82.
Shih-Hsien C., Tzu-Piao T., Kuo-Tsung H.: Improvement of Aluminum Erosion Behavior and Corrosion Resistance of AISI H13 Tool Steel by Oxidation Treatment, ISIJ International, 2010, Vol. 50, pp. 569–573
Kwok C. T., Cheng F. T., Man H. C.: Microstructure and corrosion behavior of laser surface-melted high-speed steels, Surface and Coatings Technology, 2007, Vol. 202, 2, pp. 336-348
Kovács D., Dobránszky J.: Effects of Thermochemical Surface Treatments on the Industrially Important Properties of X2CrNiMo 17-12-2 Austenitic Stainless Steel, Periodica Polytechnica Mechanical Engineering, 2019, 63(3), pp. 214–219, Budapest
voestalpine BÖHLER Edelstahl GmbH & Co KG, BÖHLER W350 ISOBLOC, https://www.bohler-edelstahl.com/en/products/w350-isobloc/, 2024.02.22
ASTM G48 – 11: Standard Test Methods for Pitting and Crevice Corrosion Resistance of Stainless Steels and Related Alloys by Use of Ferric Chloride Solution, 2015