Politejsav reaktív szívósítása

Reactive toughening of poly(lactic acid)

Abstract

Poly(ethylene-n-butylene-acrylate-co-glycidyl methacrylate) (EBA‑GMA) has been successfully used as a reactive toughening agent for poly(lactic acid) (PLA). The effectiveness of the reactive compatibilization was noticeably enhanced by using optimized processing conditions. The elevated melt-blending temperature promoted the reactive compatibilization but may have accelerated the degradation of PLA during processing at the same time. Therefore, the effect of blending temperature was optimized in terms of the mechanical properties of the PLA/EBA-GMA blends, while corresponding changes in the crystalline structure, phase morphology, and rheology were explored.

Kivonat

Jelen munkánk során etilén-N-butil-akrilát-glicidil-metakrilátot (EBA‑GMA) sikeresen alkalmaztunk, mint politejsav (PLA) reaktív szívósító adalék. Az eredmények azt mutatták, hogy a reaktív kompatibilizáció hatékonysága jelentősen megnövekedett a gyártási paraméterek optimalizálásával. A megemelt gyártási hőmérséklet elősegítette a reaktív kompatibilizáció kialakulását, ugyanakkor megnövelte a politejsav degradációjának lehetőségét is. Ezért az extrúziós hőmérséklet hatását optimalizáltuk a PLA/EBA-GMA blendek mechanikai tulajdonságainak szempontjából, miközben a kristályszerkezet, morfológiai és reológiai tulajdonságok változását vizsgáltuk.