Alumínium fémhabok koptatási vizsgálata Pin on Disc módszerrel
Abrasion test of aluminium foams by Pin on Disc method
Keywords:
metal foam, closed cell, aluminium, tribology, /, fémhab, zárt cella, alumínium, tribológiaAbstract
Open and closed-cell aluminum foams are special because of their mechanical and physical properties. The abrasion test was performed on closed-cell metal foam specimens manufactured under industrial conditions as well as those produced by our experiments. The captured specimens under different loading forces were abraded on rotated structural steel discs at different speeds. From the measured data, we calculated the coefficient of friction, the average of the coefficient of friction as a function of the surface load. In the different sections of the friction path, the minimum, maximum, and the average of the friction factor were determined. Abrasion results were summarized, compared, and analyzed.
Kivonat
A nyílt és zártcellás szerkezetű alumínium fémhabok különlegesek mechanikai és fizikai tulajdonságuk miatt. Ipari körülmények között gyártott, valamint saját kísérletek által előállított zárt cellás fémhab próbatesteken végeztünk koptatási vizsgálatot. A befogott próbatesteket különböző terhelő erők alatt, különböző sebességgel forgó szerkezeti acél tárcsán koptattuk. A mért adatokból kiszámoltuk a súrlódási tényezőt, a súrlódási tényező átlagot a felületi terhelés függvényében. A súrlódási út, különböző szakaszaiban meghatároztuk a súrlódási tényező minimumát, maximumát illetve átlagát. Összefoglaltuk, összehasonlítottuk és elemeztük a koptatási eredményeket.
References
Gyöngyösi Sz., Gábora A., Balogh G., Kalácska G., Bubonyi T., Mankovits T. Effects of Additives on the Mechanical Properties of Aluminum Foams, Mechanism and Machine Science. Springer, 2022, 109, 307-313.
Ali H., Gábora a., Naem M. A., Kalácska G., Mankovits G. Effect of the manufacturing parameters on the pore size and porosity of closed-cell hybrid aluminum foams. International Review of Applied Sciences and Engineering. Akadémiai Kiadó, 2021, 12/3, 230-237.
Kalácska Á., Székely L., Keresztes R. Z., Gábora A., Mankovits T., De Baets P. Abrasive Sensitivity of Martensitic and a Multi-Phase Steels under Different Abrasive Conditions. Materials, 2021, 14, 1343.
Gábora A., Bubonyi T., Gyöngyösi Sz. Zárt cellás alumíniumhabok pórusszerkezetének számítógépi képelemzéses vizsgálata. Anyagmérnöki Tudományok. Miskolci Egyetem, 2020, 40/1, 40-48.
Gábora A., Kalácska G., Keresztes R. Z., Beke s., Géresi Z. G. Pin on Disc vizsgálatok zártcellás alumíniumhabokon. International Journal of Engineering and Management Sciences. Debreceni Egyetem, 2020, 5/2, 353-357.
ASTM G132-96 (2013). Standard Test Method for Pin Abrasion Testing. ASTM International West Conshohocken, PA, USA, 2013.