Intenzíven képlékeny alakított lemezek további konvencionális képlékenyalakításának hatása a felületi alakváltozás homogenitására

The Effect of Subsequent Conventional Plastic Deformation on the Homogeneity of Surface Strain in Severely Plastically Deformed Sheet

Absztrakt

Aluminum sheets produced by severe plastic deformation (SPD), specifically friction-assisted lateral extrusion (FALEP), exhibit outstanding strength properties due to their ultrafine-grained microstructure (UFG). However, due to the inherent characteristics of the process, the microstructural and mechanical properties of the sheets often show an inhomogeneous distribution. The objective of the present research is to investigate how subsequent conventional plastic deformation processes—such as cold rolling—affect the distribution of surface strain fields. During tensile testing, the surface strain of Al 1050 sheets produced by both severe and conventional plastic deformation was evaluated using a digital image correlation (DIC) system.

Kivonat

Az intenzív képlékeny alakítással (SPD), ezen belül a súrlódással segített keresztirányú extrúzióval (FALEP) előállított alumíniumlemezek kiemelkedő szilárdsági mutatókkal rendelkeznek az ultrafinom szemcsés anyagszerkezetnek (UFG) köszönhetően. Ugyanakkor az eljárás sajátosságából adódóan a lemezek mikroszerkezeti és mechanikai jellemzői gyakran inhomogén eloszlást mutatnak. Jelen kutatás célja annak megfigyelése, hogy az utólagos, konvencionális képlékeny alakítási folyamatok – mint például a hideghengerlés – milyen hatással vannak a felületi alakváltozási mezők eloszlására. Az intenzív és hagyományos képlékeny alakítással előállított Al 1050 lemezeken, szakítóvizsgálat során, a felületi alakváltozást digitális képkorrelációs (DIC) rendszerrel mértük.