Az impulzusfrekvencia hatása kézi lézeres hegesztés esetén

The effects of the pulse frequency in case of manual laser welding

Abstract

The aim of our research was to study the effect of pulse frequency on the weld geometry in modulation mode manual laser welding. Increasing the pulse frequency led to a decrease in weld width and weld area. For example, the weld width decreased from 1.6 mm to less than 1.1 mm by increasing the pulse frequency from 10 Hz to 400 Hz. The weld depth did not change with the change in pulse frequency, as a full penetration weld was obtained at the set parameters for a wall thickness of 1.4 mm. When pulse frequency values of 50 Hz and below were set, huge porosities were formed in the welds, none of these welds being acceptable at any of the quality levels.

Kivonat

Kutatómunkánk során az impulzusfrekvencia varratgeometriára gyakorolt hatásának vizsgálata volt a célunk modulált üzemmódú kézi lézeres hegesztés esetén. Az impulzusfrekvencia növelése a varratszélesség és a varratterület csökkenéséhez vezetett. A varratszélesség például 1,6 mm-ről 1,1 mm alá csökkent az impulzusfrekvencia 10 Hz-ről 400 Hz-re való növelésével. A varratmélység az impulzusfrekvencia változtatásával nem változott, hiszen a beállított paraméterek mellett teljes átolvadású varrat keletkezett 1,4 mm falvastagság esetén. Az 50 Hz-es és az alatti impulzusfrekvencia értékek beállítása esetén hatalmas porozitások alakultak ki a varratokban, ezen varratok egyike sem fogadható el egyik átvételi szinten sem.