Keményforrasztott nyílt cellás alumínium habok gyártása és a létrehozott kötés minőségének vizsgálata

Manufacturing of brazed open-cell aluminum foams and testing the quality of the created bond

Abstract

This research focused on creating a durable bond between open-cell aluminum metal foams using brazing technology. Based on the measurements used to test the quality of the brazing, a strong bond was formed between the brazing sheet and the aluminum foam. The brazing also improved the foam's resistance to bending without drastic changes to other physical properties, such as their density. The maximum stress value during the bending of the brazed foams was an average of ~54 % higher compared to the infiltrated pure aluminum foams, meanwhile the increase in the density was only ~16 %. The relative density of the brazed aluminum foams compared to the bulk aluminum was ~44 %.

Kivonat

A kutatásunk nyílt cellás alumínium fémhabok közötti tartós kötés kialakítását tűzte ki célul, keményforrasztási technológiát alkalmazva. A forrasztás tesztelésére szolgáló mérések alapján a stabil, kohéziós kötés alakult ki a forraszlemez és az alumíniumhab között, illetve sikerült javítani a fémhab hajlítással szembeni ellenállását további fizikai jellemzők, mint például a sűrűség drasztikus változtatása nélkül. A forrasztott darabok hajlítás során felvett maximális feszültségértéke átlagosan ~54%-kal nőtt az infiltrált ötvözetlen alumínium habhoz képest, míg a sűrűsége csupán ~16%-kal növekedett meg. A forrasztott alumíniumhab relatív sűrűsége a tömbi alumíniumhoz képest ~44% volt.