Additívan gyártott 316L próbatestek elektrokémiai korróziós vizsgálata
Electrochemical corrosion measurements of additively manufactured 316L specimens
Keywords:
additive manufacturing, laser powder bed fusion, corrosion, stainless steel, heat treatment, /, additív gyártás, lézersugaras porágyolvasztás, korrózió, rozsdamentes acél, hőkezelésAbstract
In my research, I investigated the corrosion properties of 316L austenitic stainless steel specimens made by laser beam powder bed fusion. The samples were fabricated with different building orientation (0°, 45°, 90°) and layer thickness of 50 µm. Two specimens were made for each direction, one of which was subjected to stress relief heat treatment immediately after fabrication. The different building orientations showed different corrosion behaviour, with the most favourable properties being obtained for samples with 0 ° build orientation.
Kivonat
Kutatásomban lézersugaras porágyolvasztással készített 316L ausztenites korrózióálló acél minták korróziós tulajdonságait vizsgáltam. A minták eltérő építési iránnyal (0°, 45°, 90°), 50 µm rétegvastagsággal készültek. Minden irányhoz két próbatest készült, amelyek közül az egyiket feszültségcsökkentő hőkezelésnek vetettem alá közvetlenül a gyártást követően. Az egyes építési irányok eltérő korróziós viselkedést mutattak, a legkedvezőbb tulajdonságokkal a 0 °-os építési irányú minták rendelkeztek.
References
MSZ EN: Korrózióálló acélok. 1. rész: A korrózióálló acélok jegyzéke. 2015.
Dr. Bödök Károly: Az ötvözetlen, gyengén és erősen ötvözött szerkezeti acélok korrózióállósága, különös tekintettel azok hegeszthetőségére. CORWELD, 1997
Outokumpu: Handbook of Stainless Steel. 2014.
Cuiling Zhao – Yuchao Bai – Yu Zhang – Xiaopeng Wang – Jun Min Xue – Hao Wang: Influence of scanning strategy and building direction on microstructure and corrosion behaviour of selective laser melted 316L stainless steel. Materials Design, 209. évf. (2021. november), 109999. p. URL https://doi.org/10.1016/j.matdes.2021.109999.
J. Bedmar – S. García-Rodríguez – M. Roldán – B. Torres – J. Rams: Effects of the heat treatment on the microstructure and corrosion behavior of 316 l stainless steel manufactured by laser powder bed fusion. Corrosion Science, 209. évf. (2022. december), 110777. p. ISSN 0010-938X. URL http://dx.doi.org/10.1016/j.corsci.2022.110777.
Ke Wang, Qi Chao, Murugesan Annasamy, Peter D. Hodgson, Sebastian Thomas, Nick Birbilis, Daniel Fabijanic, On the pitting behaviour of laser powder bed fusion prepared 316L stainless steel upon post-processing heat treatments, Corrosion Science, Volume 197, 2022, 110060, ISSN 0010-938X, URLhttps://doi.org/10.1016/j.corsci.2021.110060.
Clara Nyby – Xiaolei Guo – James E. Saal – Szu-Chia Chien – Angela Y. Gerard – Huibin Ke – Tianshu Li – Pin Lu – Christian Oberdorfer – Sarita Sahu – Sirui Li – Christopher D. Taylor – Wolfgang Windl – John R. Scully – Gerald S. Frankel: Electrochemical metrics for corrosion resistant alloys. Scientific Data, 8. évf. (2021. február) 1. sz. ISSN 2052-4463. URL http://dx.doi.org/10.1038/s41597-021-00840-y.