Alkáliföldfém-titanátok fotokatalitikus fertőtlenítő hatékonysága

Photocatalytic disinfection efficiency of alkaline earth metal titanates

Abstract

Alkaline earth metal titanate photocatalysts (CaTiO₃, SrTiO₃, BaTiO₃) were hydrothermally synthesized to evaluate their photocatalytic disinfection efficiency using Gram-negative Escherichia coli and Gram-positive Bacillus licheniformis bacteria under UV-A light irradiation. PL results showed that the prepared CaTiO₃ and SrTiO₃ generated ~2.5 and ~4 times more ∙OH than our BaTiO₃ and commercial references, resulting in higher photocatalytic disinfection efficiency, comparable to that of UV light. It was found that alkaline earth metal titanates are unlikely to cause harm to microorganisms in surface or groundwater bodies without undergoing structural or other changes.

Kivonat

Alkáliföldfém-titanát fotokatalizátorokat (CaTiO₃, SrTiO₃, BaTiO₃) állítottunk elő hidrotermális módszerrel, hogy felmérjük azok fotokatalitikus fertőtlenítő hatékonyságát Gram-negatív Escherichia coli és Gram-pozitív Bacillus licheniformis baktériumokkal UV fénnyel történő gerjesztés mellett. A PL eredmények alapján az általunk előállított CaTiO₃ és SrTiO₃ ~2.5, illetve ~4-szer több hidroxilgyököt termelt, mint az általunk készített BaTiO₃ és a kereskedelmi referenciák, ami nagyobb, az UV fénnyel összemérhető fertőtlenítő hatékonyságot eredményezett. Megállapítottuk, hogy az alkáliföldfém-titanátok szerkezeti vagy egyéb változások nélkül valószínűtlen, hogy a felszíni és talajvizekben levő mikroorganizmusokat károsítsák.