Development of injection molded all-polypropylene composites with amorphous poly-alpha-olefin matrix

  • László József VARGA
  • Tamás BÁRÁNY
Keywords: Önerősített polimer kompozit, fröccsöntés, polipropilén, impregnálás, konszolidáció

Abstract

The goal of this study is to produce injection molded all-polypropylene composites at a low injection temperature. As a matrix, we used an amorphous poly-alpha-olefin-based melt-adhesive, as its melting temperature is significantly lower than the melting temperature of the polypropylene homopolymer reinforcement. The composites were produced by injection molding of an impregnated pre-product, and by overmolding of the reinforcing fabric. The composites made of the impregnated pre-product showed unsatisfactory mechanical properties, so the latter method seems to be more promising.

Kivonat

A kutatás célja alacsony hőmérsékleten fröccsönthető önerősített kompozitok kifejlesztése. Mátrixként amorf poli-alfa-olefin tartalmú ömledékragasztót használtunk, amelynek az olvadási hőmérséklete a polipropilén homopolimer erősítőanyagénál lényegesen alacsonyabb. A kompozitokat extrúziós impregnálással készült előgyártmány fröccsöntésével, valamint a mátrix szövetre történő ráfröcssöntésével állítottuk elő. Az impregnált előgyártmányból készült kompozit statikus és dinamikus tulajdonságai nem kielégítőek, ezért a két módszer közül az utóbbi bizonyult ígéretesebbnek.

References

Kmetty Á., Bárány T., Karger-Kocsis J.: Self-reinforced polymeric materials: A review. Progress in Polymer Science, 35, 1288-1310 (2010).

Capiati N. J., Porter R. S.: The concept of one polymer composites modelled with high density polyethylene. Journal of Material Science, 10, 1671-1677 (1975).

Ward I. M., Hine P. J.: The science and technology of hot compaction. Polymer, 45, 1413-1427 (2004)

Peijs T.: Composites for recyclability. Materials Today, 6, 30-35 (2003).

Bárány T., Izer A., Czigány T.: High performance self-reinforced polypropylene composites. Materials Science Forum, 537-538, 121-128 (2007).

Bárány T., Izer A., Czigány T.: On consolidation of self-reinforced polypropylene composites. Plastic, Rubber and Composites, 35, 375-379 (2006)

Karger-Kocsis J., Bárány T.: Single-polymer composites (SPCs): Status and future trends. Composites Science and Technology, 92, 77-94 (2014).

KmettyÁ., Tábi T., Kovács J. G., Bárány T.: Development and characterization of injection molded, all-polypropylene composites. Express Polymer Letters, 7, 134-145 (2013).

Andrzejewsky J., Szostak M., Barczewsky M., Krasucki J., Sterzynski T.: Fabrication of the self-reinforced composites using co-extrusion technique. Journal of Applied Polymer Science, 131 (2014).

Wang J., Wang S., Chen D.: Development and characterization of insert injection moulded polypropylene single-polymer composites with sandwiched wovenfabric. Composites Science and Technology, 117, 18-25 (2015).

Prox M., Pornnimit B., Varga J., Ehrenstein G. W.: Thermoanalytical investigations of self-reinforced polyethylene. Journal of Thermal Analysis, 36, 1675-1684 (1990).

Sustic A.: Amorphous poly alpha olefin (APAO) based hot melts. ASC hot melt short course, New Orleans, Egyesült Államok (2016).

Published
2020-04-16
How to Cite
[1]
VARGA, L. and BÁRÁNY, T. 2020. Fröccsöntött amorf poli-alfa-olefin mátrixú önerősített kompozit fejlesztése. Nemzetközi Gépészeti Konferencia – OGÉT. 28, (Apr. 2020), 89-92.
Section
A. szekció - Anyagtudomány és technológia