Dolomit tartalmú szálerősített epoxi kompozitok vizsgálata

Analysis of dolomite-filled fiber reinforced epoxy composites

  • Tej SINGH
  • Gusztáv FEKETE
  • Endre JÁNOSI
Keywords: epoxi kompozitok, szálerősítés, dolomit

Abstract

One method for the development of the mechanical properties of composites is to integrate different substances into the polymer matrix to improve mechanical and erosion properties.  In our paper, dolomite is recommended as an additive to improve the properties of fibre-reinforced epoxy composites. The analysed composites were developed in a wooden mold by using conventional handlayup procedure. The dolomite-filled fiber reinforced composites were evaluated for physical and mechanical properties. Densities (both experimental and theoretical) and void content of manufactured composites were found to increase with increased dolomite content. With the addition of dolomite, the hardness improves with a decrease in tensile strength.

Kivonat

A kompozitok mechanikai tulajdonságainak fejlesztésére az egyik módszer a különböző anyagoknak a polimer mátrixba történő integrálása, a mechanikai és eróziós tulajdonságok javításának érdekében. Dolgozatunkban a szálerősített epoxi kompozitok tulajdonságainak javítására a dolomitot javasoljuk adalékanyagként. A vizsgált kompozitok fa őntőforma segítségével készültek a hagyományos eljárás alapján. A dolomit tartalmú szálerősítésű kompozitokat fizikai és mechanikai tulajdonságokra vizsgáltuk. A gyártott kompozitok sűrűségének (kísérleti és elméleti) és porozitásának emelkedését észleltük a dolomit-tartalom növekedésével. A dolomit hozzáadásával a keménység emelkedett, a szakító szilárdság csökkenése mellett. 

References

Patnaik A, Satapathy A, Mahapatra S S and Dash R R :A comparative study on different ceramic fillers affecting mechanical properties of glass-polyester composites J. Reinf. Plast. Compos, 2009.

KiranMD, GovindarajuHKand Jayaraju T:Evaluation of mechanical properties of glass fiber reinforced epoxy polymer, 2018.

Singha A S and Thakur V K: Synthesis and characterization of short Grewia optiva fiber‐based polymer composites Polym.Compos, 2010.

Karaca S, Gurses A, Ejder M and Acikyildis D: Absorptive removal of phosphate from aqueous solutions using raw and calcinated, 2006.

Ye H, Fu Cand Yang G: Influence of dolomite on the properties and microstructure of alkali-activated slag with and without pulverized fly ash Cem. Concr. Compos, 2019.

Judawisastra H, Sitohang RDR and RosadiMS:Water absorption and tensile strengt degradation of Petung bamboo,2017.

ASTM D2734-16, Standard Test Methods for Void Content of Reinforced Plastics, ASTM International, West Conshohocken, PA, 2016.

ASTMD785-15, Standard Test Method for Rockwell Hardness of Plastics and Electrical Insulating Materials, ASTM International, West Conshohocken, PA, 2015.

Shashi Kant Verma, Ashutosh Gupta, Tej Singh,Brijesh Gangil, Endre Jánosi, Gusztáv Fekete: Influenceof dolomite on mechanical, physical and erosive wear properties of natural-synthetic fiber reinforced epoxy composites, Mater. Res. Express 6 (2019).

ISO 527-2:2012 Plastics -Determination of tensile properties -Part 2: Test conditions for moulding and extrusion plastics

Published
2020-04-16
How to Cite
[1]
SINGH, T., FEKETE, G. and JÁNOSI, E. 2020. Dolomit tartalmú szálerősített epoxi kompozitok vizsgálata. Nemzetközi Gépészeti Konferencia – OGÉT. 28, (Apr. 2020), 77-80.
Section
A. szekció - Anyagtudomány és technológia