Az AlNiCo és NbFeB mágneses anyagok korróziós viselkedése sósavban / Corrosion Behavior of AlNiCo and NdFeB Magnetic Materials in Hydrochloric Acid

Delia PATROI, Sorina MITREA, Mónika LINGVAY, József LINGVAY

Összefoglaló


The corrosion behavior in 1% hydrochloric acid solution of AlNiCo (aluminum, nickel and cobaltbased
alloys) and the sintered NdFeB-type magnetic materials was investigated in magnetized and not
magnetized state. The XRD and SEM microscopy determinations have shown that the investigated materials is
homogeneous structured. – the FeCo and AlNi respectively the Nd2Fe14B and α Fe crystallites is evenly
distributed. The gravimetric and XRF determinations showed that the corrosion rate of investigated materials
in magnetized state is greater than the in non-magnetized state (AlNiCo - approx. 3 times, NdFeB approx. 4.3
times)..

ÖSSZEFOGLALÓ
Az AlNiCo (alumínium, nikkel és kobalt alapú ötvözet) valamint a szinterezett NdFeB típusú mágneses
anyagok korróziós viselkedését vizsgáltuk 1%-os sósavoldatban, telítettségig mágnesezett, és nem mágnesezett
állapotban. Az XRD és SEM mikrószkópiás meghatározások kimutatták, hogy a megvizsgált anyagok szerkezete
homogén – ezekben a FeCo és AlNi, illetve Nd2Fe14B és α Fe krisztalitok egyenletesen oszlanak el. A gravimetriás
és XRF meghatározások kimutatták, hogy telítettségig mágnesezett állapotban a megvizsgált anyagok
korróziósebessége nagyobb mint nem mágnesezett állapotban (AlNiCo kb. 3-szor, NdFeB kb. 4,3-szor).

Kulcsszavak


Alnico magnets, NdFeB magnets, corrosion, hydrochloric acid / Alnico mágnesek, NdFeB mágnesek, korrózió, sósav

Teljes szöveg:

PDF

Bibliográfiai hivatkozások


O. Gutfleisch, M.A. Willard, E. Brück, C.H. Chen, S.G. Shankar, J.P. Liu: Magnetic materials and devices for the

st century: stronger, lighter, and more energy efficient. Adv. Mater. 2011. 23, 821–842.

N. Yogal, C. Lehrmann: Study of Magnetic Properties on the Corrosion Behavior and Influence of Temperature in

Permanent Magnet (Nd-Fe-B) Used in PMSM. International Journal of Electrical, Computer, Energetic, Electronic

and Communication Engineering 2014. 8. (11) 1592 – 1596

W. Kappel, M. M. Codescu, N. Stancu, D. Popa: Evaluation of the corrosion behaviour for the permanent magnets

based on rare earths, used in aeronautical industry. Journal of optoelectronics and advanced materials, 2006. 8. (2)

– 525

M. M. Codescu, W. Kappel, M. Dumitrache, D. Popa: Corrosion tests on alloys and permanent magnets based on

NdFeB, used in aerospace industry, Journal of optoelectronics and advanced materials. 2008. 10. (4) 790 – 793

Kalyan Chitrada, Krishnan S. Raja, Batric Pesic, Indrajit Charit: Corrosion Behavior of Surface Modified NdFeB

Permanent Magnet inDilute Chloride Environments. Electrochimica Acta 2014. (123) 23–32

E. Isotahdon, E. Huttunen-Saarivirta, S. Heinonen, V.-T. Kuokkala, M. Paju: Corrosion mechanisms of sintered

Nd–Fe–B magnets in the presence of water as vapour, pressurised vapour and liquid. Journal of Alloys and

Compounds 2015. (626) 349–359

C. Gaona-Tiburcio, F. Almeraya-Calderón, J.G. Chacon-Nava, J.A. Matutes-Aquino, A. Martinez-Villafañe:

Electrochemical response of permanent magnets in different solutions. Journal of Alloys and Compounds. 2004.

(369) 78–80

R. Sueptitz, K. Tschulik, M. Uhlemann, M. Katter, L. Schultz, A. Gebert: Effect of magnetization state on the

corrosion behaviour of NdFeB permanent magnets. Corrosion Science. 2011. 53. 2843–2852

Elena Radu, Delia Patroi, Gabriela Oprina, Andreea Voina, Iosif Lingvay, Comparative Studies on Aspergillus

niger Biocorrosion of Alnico and NdFeB Magnetic Materials, REV.CHIM.(Bucharest) Vol. 67 (10) 2016. pp.

-1978

Gánóczy József: Rendhagyó (?) korrózió – Amikor a vegyileg ellenálló acél mégsem korrózióálló. 2010. (5-6) pp.

-137.


Refbacks

  • There are currently no refbacks.


ISSN Print: 1454-0746; ISSN Online: 2458-0201